Designation: D 882 – 02
Standard Test Method for
Tensile Properties of Thin Plastic Sheeting1
This standard is issued under the fixed designation D 882; the number immediay following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon （e） indicates an editorial change since the last revision or reapproval.
These test methods have been approved for use by agencies of the Department of Defense to replace Method 1013 of Federal Test
Method Standard 406.
1. Scope *
1.1 This test method covers the determination of tensile
properties of plastics in the form of thin sheeting, including
film （less than 1.0 mm （0.04 in.） in thickness）.
NOTE 1—Film has been arbitrarily defined as sheeting having nominal
thickness not greater than 0.25 mm （0.010 in.）.
NOTE 2—Tensile properties of plastics 1.0 mm （0.04 in.） or greater in
thickness shall be determined according to Test Method D 638.
1.2 This test method may be used to test all plastics within
the thickness range described and the capacity of the machine
employed.
1.2.1 Static Weighing, Constant-Rate-of-Grip Separation
Test—This test method employs a constant rate of separation of
the grips holding the ends of the test specimen.
1.3 Specimen extension may be measured in these test
methods by grip separation, extension indicators, or displacement
of gage marks.
1.4 A procedure for determining the tensile modulus of
elasticity is included at one strain rate.
NOTE 3—The modulus determination is generally based on the use of
grip separation as a measure of extension; however, the desirability of
using extensometers, as described in 5.2, is recognized and provision for
the use of such instrumentation is incorporated in the procedure.
1.5 Test data obtained by this test method is relevant and
appropriate for use in engineering design.
1.6 The values stated in SI units are to be regarded as the
standard. The values in parentheses are provided for information
only.
1.7 This standard does not purport to address all of the
safety concerns, if any, associated with its use. It is the
responsibility of the user of this standard to establish appropriate
safety and health practices and determine the applicability
of regulatory limitations prior to use.
NOTE 4—This test method is similar to ISO 527-3, but is not considered
technically equivalent. ISO 527-3 allows for additional specimen configurations,
specifies different test speeds, and requires an extensometer or
gage marks on the specimen.
2. Referenced Documents
2.1 ASTM Standards:
D 618 Practice for Conditioning Plastics for Testing2
D 638 Test Method for Tensile Properties of Plastics2
D 4000 Classification System for Specifying Plastic Materials3
D 5947 Test Methods for Physical Dimensions of Solid
Plastic Specimens4
D 6287 Practice for Cutting Film and Sheeting Test Specimens4
E 4 Practices for Force Verification of Testing Machines5
E 691 Practice for Conducting an Interlaboratory Study to
Determine the Precision of a Test Method6
2.2 ISO Standard:
ISO 527-3 Plastics—Determination of Tensile Properties—
Part 3: Test Conditions for Films and Sheets7
3. Terminology
3.1 Definitions—Definitions of terms and symbols relating
to tension testing of plastics appear in the Annex to Test
Method D 638.
3.1.1 line grips—grips having faces designed to concentrate
the entire gripping force along a single line perpendicular to the
direction of testing stress. This is usually done by combining
one standard flat face and an opposing face from which
protrudes a half-round.
3.1.2 tear failure—a tensile failure characterized by fracture
initiating at one edge of the specimen and progressing across
the specimen at a rate slow enough to produce an anomalous
load-deformation curve.
4. Significance and Use
4.1 Tensile properties determined by this test method are of
1 These test methods are under the jurisdiction of ASTM Committee D20 on
Plastics and are the direct responsibility of Subcommittee D20.10 on Mechanical
Properties.
Current edition approved April 10, 2002. Published June 2002. Originally
published as D 882 – 46 T. Last previous edition D 882 – 01.
2 Annual Book of ASTM Standards, Vol 08.01.
3 Annual Book of ASTM Standards, Vol 08.02.
4 Annual Book of ASTM Standards, Vol 08.03.
5 Annual Book of ASTM Standards, Vol 03.01.
6 Annual Book of ASTM Standards, Vol 14.02.
7 Available from American National Standards Institute, 25 W. 43rd St., 4th
Floor, New York, NY 10036.
1
*A Summary of Changes section appears at the end of this standard.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.