合金分析儀中合金結構鋼牌號及化學成分表
鋼組 | 牌號 | 化學成分,% | |||||
C | Si | Mn | Mo | W | Cr | ||
Cr | 15 Cr | 0.12~0.18 | 0.17~0.37 | 0.40~.070 | - | - | 0.70~1.00 |
| 15 CrA | 0.12~0.17 | 0.17~0.37 | 0.40~0.70 | - | - | 0.70~1.00 |
| 20 Cr | 0.18~0.24 | 0.17~0.37 | 0.50~0.80 | - | - | 0.70~1.00 |
| 30Cr | 0.27~0.34 | 0.17~0.37 | 0.50~0.80 | - | - | 0.80~1.10 |
| 35 Cr | 0.32~0.39 | 0.17~0.37 | 0.50~0.80 | - | - | 0.80~1.10 |
| 40Cr | 0.37~0.44 | 0.17~0.37 | 0.50~0.80 | - | - | 0.80~1.10 |
| 45Cr | 0.42~0.49 | 0.17~0.37 | 0.50~0.80 | - | - | 0.80~1.10 |
| 50Cr | 0.47~0.54 | 0.17~0.37 | 0.50~.080 | - | - | 0.80~1.10 |
CrSi | 38CrSi | 0.35~0.43 | 1.00~1.30 | 0.30~0.60 | - | - | 1.30~1.60 |
| 12CrMo | 0.08~0.15 | 0.17~.037 | 0.40~0.70 | 0.40~0.55 | - | 0.40~0.70 |
| 15CrMo | 0.12~0.18 | 0.17~0.37 | 0.40~0.70 | 0.40~0.55 | - | 0.80~1.10 |
| 20CrMo | 0.17~0.24 | 0.17~0.37 | 0.40~0.70 | 0.15~0.25 | - | 0.80~1.10 |
| 30CrMo | 0.26~0.34 | 0.17~0.37 | 0.40~0.70 | 0.15~0.25 | - | 0.80~1.10 |
| 30CrMoA | 0.26~0.33 | 0.17~0.37 | 0.40~0.70 | 0.15~0.25 | - | 0.80~1.10 |
CrMo | 35CrMo | 0.32~0.40 | 0.17~0.37 | 0.40~0.70 | 0.15~0.25 | - | 0.80~1.10 |
| 42CrMo | 0.38~0.45 | 0.17~0.37 | 0.50~0.80 | 0.15~0.25 | - | 0.90~1.20 |
南京固琦分析儀器制造有限公司
09.11.03
上一篇:ZO型氧化鋯系列產品-怎樣選型
下一篇:以太網交換機的介紹
全年征稿/資訊合作
聯系郵箱:1271141964@qq.com
免責聲明
- 凡本網注明"來源:智能制造網"的所有作品,版權均屬于智能制造網,轉載請必須注明智能制造網,http://www.xashilian.com。違反者本網將追究相關法律責任。
- 企業發布的公司新聞、技術文章、資料下載等內容,如涉及侵權、違規遭投訴的,一律由發布企業自行承擔責任,本網有權刪除內容并追溯責任。
- 本網轉載并注明自其它來源的作品,目的在于傳遞更多信息,并不代表本網贊同其觀點或證實其內容的真實性,不承擔此類作品侵權行為的直接責任及連帶責任。其他媒體、網站或個人從本網轉載時,必須保留本網注明的作品來源,并自負版權等法律責任。
- 如涉及作品內容、版權等問題,請在作品發表之日起一周內與本網聯系,否則視為放棄相關權利。
2025中國鄭州衡器與計量技術設備展覽會
展會城市:鄭州市展會時間:2025-11-07